CDA630高硬度镍铝青铜板

CDA630铝青铜铸造铝青铜说明结构材料。使用温度在-200°C~+200°C之间

主要用途：机械受力部件：杠杆，外壳，衬套，电气行业的碳刷夹板，家具行业的配件，纺织机械和汽车行业的小齿轮、锥齿轮，同步环，切换装置和换挡拨叉密度7.5 g/cm3

Chemical compositionCu%Fe%Ni%1Al%Mn%





 

Chemical composition according to ASTM B505/B505M-18

1Ni value includes Co.

Note: Cu + sum of named elements, 99.5% min. Unless otherwise noted, single values represent maximums.

78.00
min3.00-
5.003.00-
5.5010.00-
11.50 
3.50






MachinabilityCopper alloy UNS No.Machinability ratingDensity (lb/in3 at 68 °F)CDA630500.272Mechanical properties

Mechanical properties according to ASTM B505/B505M-18

铝青铜的典型使用

　　-阀茎、泵轴、密封腺体,防喷器部分

　　,起落架衬套及轴承、皮瓣衬套,致动器,部分,支撑套管

　　汽车气门,气门座

　　其他工业——球、齿轮、凸轮、轴系、发电站的冷凝器管和脱盐装置,气门座,气门,泵轴、结构成员,、热交换器、头,换热器法兰、轴承、轴套、阀球,液压衬套为地球移动设备、耐腐蚀的文章,飞机零件、焊接管

　它们是QAl5、QAl7、QAl9-2、QAl9-4、QAl9-5-1-1、QAl10-3-1.5、QAl10-4-4、QAl10-5-5、QAl11-6-6.而美国ASTM标准中加工铝青铜共有26，铸造合金有18个。铝青铜的基本合金组成为Cu-Al、Cu-Al-Fe、Cu-Al-Ni、Cu-Al-Fe-Ni、Cu-Al-Fe-Ni-Mn等。

公司常年备现货库存。欢迎各界人士莅临参观指导！！！

UNS No. C95200; UNS No. CuAl10Fe5Ni5-C; UNS No. CuAl10Fe5Ni5-C; UNS No. C95410; UNS No. C95500; UNS No. CuAl10Fe5Ni5-C; UNS No. C95600; UNS No. C95700; UNS No. CuAl10Fe5Ni5-C; UNS No. C95820; and UNS No. C95900.

(In Tension)

Imperial

Metric

Density

0.274lb/in³ @ 68º F

7580 kg/m³ @ 20ºC

Specific Gravity

7.58

7.58

Specific Heat

0.090 Btu/lb º F @68º F

376.7 J/kg ºC @20 ºC

Electrical Conductivity

7% IACS @ 68º F

0.041mega Siemens/cm @20 ºC

Thermal Conductivity

22.6 Btu.ft(hr.ft² º F) @68º F

0.391W/cm ºC @20 ºC

Thermal Expansion

9.0 x10ˉ 6 per º F (68-572 º F )

15.5 x10ˉ 6 perºC (20-300 ºC)

Electrical Resistivity

116Ω-cmil/ft @ 68º F

19.28 µ Ω-cm@20 ºC

Relative Magnetic Permeability

1.4µ

Machining Index

20 (Based on free machining brass )

Modulus of Rigidity

6800ksi

46884MPa

Modulus of Elasticity

18200ksi

125484MPa

Melting Range

1920-1960 ºF

1049-1071ºC

Hot Working Range

1450-1700 ºF

788-927 ºC

Cold Working

Limited

Cryogenic

Retains properties down to – 302 ºF

(-190 ºC)

Elevated Temperatures

Retains properties to 662 ºF

(350 ºC)